Ⅰ: Ta dig att veta 5052 Slitbana i legerad aluminium.

Ⅰ-A: 5052 Detaljer för slitbanan i legerad aluminium.

5052 är en platta av aluminium-magnesiumlegering, ljustäthet för plattans mönster av aluminiumlegering, lämplig för den populära trenden med lättviktsbilar, skåpbilar, brandbilar, specialfordon, speciella fordon och andra botten eller innervägg används ofta denna serie av aluminium-magnesiumlegering plåt, effective weight reduction, high hardness, corrosion resistance.

Aluminum – magnesium alloy also contains a small amount of manganese, chromium, beryllium, titanium, etc.. Manganese in the alloy in addition to a small amount of solid solution, most of the formation of MnAl6. In 5052 aluminum pattern plate chromium role similar to manganese, improve the stress corrosion cracking resistance, improve the base metal and weld strength, reduce the tendency of welding cracks, but its content generally does not exceed 0.35%.

5052 Slitbana i legerad aluminium

Ⅰ-B: The Difference Of Aluminum Plate & Aluminum Sheet.

Aluminum sheet and aluminum plate are essentially the same; the only true distinction is in their respective thickness. Aluminum sheet is any aluminum sheet metal thicker than foil but thinner than 6mm; it comes in many forms including diamond plate, expanded, perforated, and painted aluminum sheet. Aluminum plate is any aluminum sheet metal that is thicker than 6mm.

Ⅰ-C: 5052 Aluminum Plate Applications.

5052 Aluminum checker plates sheets are very resilient against aggressive substances and therefore, they regarded as indestructible. Whether industrial floors, flygplan, ships and vehicles, or stairs indoors or outdoors -5052 aluminium checker plates are a popular material which is appreciated for its excellent properties, the high resilience and the low weight.

Aluminum plate 5052 is used in many types of industrial applications, including:

  • 1.Refrigerator liners
  • 2.Fuel tanks
  • 3.Storm shutters
  • 4.Panels
  • 5.Road signs
  • 6.Marine applications
  • 7.Medical equipment
  • 8.Marine hardware
  • 9.Boat hulls
  • 10.Drums
  • 11.And more
  • Ⅱ: Parameters Of 5052 Slitbana i legerad aluminium.

    Ⅱ-A: Parameters Of 5052 Slitbana i legerad aluminium.

    Product equivalent name: rutig plåt av aluminium, aluminum chequer plates
    Alloy equivalent name: a5052, 5052a, aa5052, 5052aa, al5052, 5052 aa, aa 5052, jis a5052p, al5052, aw5052 grade etc
    Soft HO, H11, H12, H13, H14, H15, H16, H17, H18, H19, H20, H21, H22, H23, H24, H25, H26, H27, H28, H29, H30, H31, H32, H33, H34, H35, H36, H37, H38, H39, H46, H111, H112, H114, H116, H131, H321 etc
    T0, T2, T3, T4, T5, T6, T7, T8, T24, T32, T35, T73, T74, T83, T351, T354, T650, T651, T851 osv

    Tjocklek: 1.8, 2.0, 2.2, 2.5, 2.7, 3.0, 4.0, 5.0 mm effective
    Size: 1250*2500, 1500*3000 etc

    The surface of patterned aluminum sheet can be anodized or black anodized

    Ⅱ-B: Chemical Of 5052 Slitbana i legerad aluminium.



























    Ⅱ-C: Aluminium 5052 Sheet and Plate Characteristics

  • 1.Non-heat treatable
  • 2.High strength/high fatigue strength
  • 3.Weldable and cold workable
  • 4.Corrosion resistant, especially for marine or saltwater applications
  • Ⅲ: Manufacture And Process Of 5052 Slitbana i legerad aluminium.

    Ⅲ-A: Manufacture Of 5052-H34 5052 Aluminum Alloy Sheet And Strip.

    The specific technical solutions are as follows:

    The production method of 5052-H34 aluminum alloy plate and strip mainly includes the following steps: casting, sawing, milling, heating, hot rolling, cold rolling, finished product, finishing;

    In the described hot rolling step, the thickness of the hot rolled coil is reserved 40%-60% according to the thickness of the finished product, and the hot roughing and finishing rolling temperature is 430-450 °C, and the hot finishing temperature is 320-350 °C;

    In the cold rolling step, after one or two passes of cold rolling to the thickness of the finished product, the general processing rate is 40-60%.

    In some embodiments, in the heating step, the ingot is cast, wherein the heating temperature is 480-520° C., and the soaking time is 2-5 hours.

    In some embodiments, in the finished product step, the temperature range is 140-200 ° C, and the soaking time is 1-5 hours.

    In some embodiments, the mass percentage of the chemical composition of the ingot is: Si≤0.15%, Fe0.15~0.30%, Cu≤0.10%, Mn≤0.08%, Mg2.3~2.7%, Cr0.15~0.25 %, Zn≤0.10%, Ti0.008~0.03%, other impurity elements alone ≤0.03%, other impurity elements combined ≤0.15%, the rest are Al; the smelting temperature is 735-755℃, the refining temperature is 720-740℃ , casting temperature 675-695 .

    Ⅲ-B: Surface Treatment Of 5052 Aluminum Alloy Sheet.

    Available Dimension

    Mill finish Surface

    Bright finish Surface




    Pattern height

    Sheet Thickness from 1.0mm to 2.0mm,  bar height: 0.50mm

    Sheet Thickness from 1.0mm to 2.0mm,  bar height: 0.50mm

    Sheet Thickness from 1.0mm to 2.0mm,  bar height: 1.00mm

    Sheet Thickness from 1.0mm to 2.0mm,  bar height: 1.00mm

    Sheet Thickness above 2.0mm,  bar height: 1.50mm

    Sheet Thickness above 2.0mm,  bar height: 1.50mm

    Bredd (mm)

    Maximum 1500mm

    Maximum 1650mm

    Längd (mm)

    Maximum 6000mm

    Maximum 6000mm

    Paper interleaves

    On request for selected

    On request for selected

    Normal size

    1200×2400mm, 1219×2438mm,  1219×3048mm

    1200×2400mm, 1219×2438mm,  1219×3048mm